产品详情
简单介绍：
50 OD (620nm abs max), supplied in USP grade purified water
详情介绍：
Product Details
Composition: Carboxyl (carboxyl-PEG-thiol, 5kDa) Gold NanoUrchins
Core Size: 80nm
Adsorption max: 620nm
OD per ml: 50 (50x more concentrated than our non-functionalized gold nanoparticles)
Particles per ml: 3.9E+11
Volume: 1ml
Nr of Carboxyl Groups on Surface: ~1/nm2
Formulation: Supplied in USP grade purified water
Core Size: 80nm
Adsorption max: 620nm
OD per ml: 50 (50x more concentrated than our non-functionalized gold nanoparticles)
Particles per ml: 3.9E+11
Volume: 1ml
Nr of Carboxyl Groups on Surface: ~1/nm2
Formulation: Supplied in USP grade purified water
Properties
Cytodiagnostics PEGylated Gold NanoUrchins with carboxyl functional groups are made using a unique proprietary protocol resulting in particles with superior size distribution and shape compared to the leading competitor (Tech Note #104) and are ideal for development of covalent gold nanourchin conjugates.
The carboxyl functionalized gold surface allows for covalent conjugation of antibodies, proteins and other ligands using standard EDC/NHS coupling chemistry.
Low batch to batch variability (+/- 2nm) assures you as a customer always end up with a product within the specified size range ordered.
All of our batches go through stringent quality control prior to shipment to our customers using dynamic light scattering to guarantee size and monodispersity and lot specifications are supplied with each product.
Storage
Store product away from direct sunlight at 4°C. Do NOT freeze. When stored as specified the product is stable for at least twelve months.
Diameter (nm) | Peak SPR Wavelength (nm) | NPS/ml* | Wt. Conc (mg/ml)* | Size Dispersity (+/-nm) | Particle Volume (nm3) | Surface Area (nm2) | Surface/ Volume Ratio | Particle Mass (g) | Molar Mass (g/mol) | Molar Concentration* | |
80 | 620 | 3.9E+11 | 2.03E+00 | <10% | 2.68E+05 | 2.01E+04 | 0.075 | 5.20E-15 | 3.13E+09 | 6.49E-10 | |
| *All concentrations as indicated at an optical density of 50 (OD=50) | |||||||||||