聚氨脂玻璃纤维套管
详细说明：PUG-301
2741聚氨酯玻璃纤维软管（符合沪Q/JBQR23-2001）
2741 Fiberglass Sleeving Coated With Polyurethane （In According With Shanghai Q/JBQR23-2001）
聚氨酯玻璃纤维软管系采用无碱玻璃纤维编织成管，并涂以改性聚氨酯树脂经加热烘干而成的F级绝缘软管。具有可靠的耐热性，良好的电性能，较好的柔软性和弹性。适用于做F级电机、电器及仪表、无线电、家用电器等装置的布线绝缘和机械保护。
长度：1000（ ）毫米（连续长度由供需双方协议）。
Fiberglass sleeving coated with polyurethane is manufactured with non-alkali fiberglass braided sleeving and coated with a layer of polyurethane and than thermoset to form F grade insulating sleeving.It possesses reliable heat resistance,good qualities of dielectric,fair softness and elasicity.It can be used for wiring insulation and machanic protection for F grade electrical machinery,electric appliances,electrical instruments,wireless sets and domestic electrical appliances.
Length:1000（ ）mm（continuous length can be negotiated）.
内径（mm） Inner Diametor
壁厚（mm） Wall Thickness
标称 Nominal
公差 Tolerance
1；1.5
±0.15
0.20
0.75
2；2.5；
±0.20
3
±0.25
4；5；6
0.30
7；8；9；10
±0.50
性能指标 Property requirements
性能Property
指标Requirements
耐焊热性 Resistance to soldering heat
通过（**内径5毫米及以下） Pass （only for sleeving having nominal bore Diameter up to and including 5mm）
加热后弯曲性 Bending after heating
不得开裂，试验温度180℃经48±1小时。 No cracking or detachment of coating shall all be visible after bending around mandrels after48±1h at 180℃
低温时的弯曲性 Bending at low temperature
不得开裂，试验温度-15℃。 No cracking or detachment of coating shall be visible after bending around mandrels while at-15℃
绝缘电阻MΩ Insulation resistance
≥103
温度指数 Temperature index
155℃
击穿电压，千伏 Breakdown Voltage kv 直芯棒25毫米电极 Straight mandrel with 25mm electrode
室温下 Room temp
高温下 Elevated temp
湿热处理后 Damp heat
中值 Central value
≥4.0
≥1.6
≥1.2
*低值 Lowest individual value
≥2.5
≥1.0
≥0.8