标准号
|
描述
|
|
ASTM C1161
|
This test method covers the determination of flexural strength of advanced ceramic materials at ambient temperature. Four-point-1/4 point and three-point loadings with prescribed spans are the standard. Rectangular specimens of prescribed cross-section sizes are used with specified features in prescribed specimen-fixture combinations.
|
|
ASTM C1211
|
This test method covers determination of the flexural strength of advanced ceramics at elevated temperatures. Four-point-1/4 point and three-point loadings with prescribed spans are the standard. Rectangular specimens of prescribed cross-section are used with specified features in prescribed specimen-fixture combinations.
|
|
ASTM C1273
|
This test method covers the determination of tensile strength under uniaxial loading of monolithic advanced ceramics at ambient temperatures.
|
|
ASTM C1291
|
This test method covers the determination of tensile creep strain, creep strain rate, and creep time-to-failure for advanced monolithic ceramics at elevated temperatures, typically between 1073 and 2073 K.
|
|
ASTM C1292
|
This test method covers the determination of shear strength of continuous fiber-reinforced ceramic composites (CFCCs) at ambient temperature.
|
|
ASTM C1323
|
This test method covers the determination of ultimate strength under monotonic loading of advanced ceramics in tubular form at ambient temperatures.
|
|
ASTM C1337
|
This test method covers the determination of the time-dependent deformation and time-to-rupture of continuous fiber-reinforced ceramic composites under constant tensile loading at elevated temperatures.
|
|
ASTM C1341
|
This test method covers the determination of flexural properties of continuous fiber-reinforced ceramic composites in the form of rectangular bars formed directly or cut from sheets, plates, or molded shapes.
|
|
ASTM C1358
|
This test method covers the determination of compressive strength including stress-strain behavior under monotonic uniaxial loading of continuous fiber-reinforced advanced ceramics at ambient temperatures.
|
|
ASTM C1359
|
This test method covers the determination of tensile strength including stress-strain behavior under monotonic uniaxial loading of continuous fiber-reinforced advanced ceramics at elevated temperatures.
|
|
ASTM C1366
|
This test method covers the determination of tensile strength under uniaxial loading of monolithic advanced ceramics at elevated temperatures.
|
|
ASTM C1425
|
This test method addresses the compression of a double-notched specimen to determine interlaminar shear strength of continuous fiber-reinforced ceramic composites (CFCCs) at elevated temperatures.
|
|
ASTM C1469
|
This test method covers the determination of shear strength of joints in advanced ceramics at ambient temperature.
|
|
ASTM C674
|
These test methods cover determination of the modulus of rupture and the modulus of elasticity of fired ceramic whitewares bodies, formed by any fabrication method, and are applicable to both glazed and unglazed test specimens.
|
|
ASTM C773
|
This test method covers two test procedures (A and B) for the determination of the compressive strength of fired whiteware materials.
|
|
|
|
BS 6431-12:1983, EN 100:1991
|
Ceramic floor and wall tiles. Method for determination of modulus of rupture.
|
|
BS EN 1892:2005
|
Advanced technical ceramics. Mechanical properties of ceramic composites at high temperature under inert atmosphere. Determination of tensile properties.
|
|
BS EN 1894:2005
|
Advanced technical ceramics. Mechanical properties of ceramic composites at high temperature under inert atmosphere. Determination of shear streng th by compression loading of notched specimens.
|
|
BS EN 658-1:1998
|
Advanced technical ceramics. Mechanical properties of ceramic composites at room temperature. Determination of tensile strength.
|
|
BS EN 658-2:2002
|
Advanced technical ceramics. Mechanical properties of ceramic composites at room temperature. Determination of compression properties.
|
|
BS EN 658-3:2002
|
Advanced technical ceramics. Mechanical properties of ceramic composites at room temperature. Determination of flexural strength.
|
|
BS EN 658-5:2002
|
Advanced technical ceramics. Mechanical properties of ceramic composites at room temperature. Determination of interlaminar shear strength by shor t span bend test (three points).
|
|
BS EN ISO 10545-4:1997
|
Ceramic tiles. Determination of modulus of rupture and breaking strength.
|
|
BS ISO 15490:2000
|
Fine ceramics (advanced ceramics, advanced technical ceramics). Test method for tensile strength of monolithic ceramics at room temperature.
|
|
|
|
EN 843-1
|
Advanced technical ceramics. Monolithic ceramics. Mechanical properties at room temperature. Part 1. Determination of flexural strength.
|
|
EN 843-2
|
Advanced technical ceramics. Monolithic ceramics. Mechanical properties at room temperature. Part 2. Determination of Young's modulus, s hear modulus and Poisson's ratio.
|
|
|
|
ISO 17565
|
Fine ceramics (advanced ceramics, advanced technical ceramics). Test method for flexural strength of monolithic ceramics at elevated te mperature
|
|
ISO 22215
|
Fine ceramics (advanced ceramics, advanced technical ceramics). Test method for tensile creep of monolithic ceramics
|